Use of immersion tin and alloys as a bonding medium for multilayer circuits

ABSTRACT

A novel immersion tin composition is disclosed containing both thiourea compounds and urea compounds. A method for improving the adhesion of printed circuit boards to one another in a multilayer board and for minimizing or eliminating smear in a multilayer board is also disclosed comprising coating the metal layers of the individual circuit boards with an immersion tin coating prior to laminating them to form a multilayer board. The immersion tin composition may also be prepared from a two component system which eliminates or substantially retards the formation of H 2  S in the presence of sulfur containing components.

Cross Reference to Related Patent Application

This patent application is a continuation-in-part of U.S. patent application Ser. No. 770,842 filed Aug. 29, 1985 now U.S. Pat. No. 4,715,894.

DESCRIPTION

1. Technical Field

The field of the invention is printed circuit boards and a method for improving the manufacture of such boards by employing a tin immersion coating. Improved adhesion of laminae in a multilayer board, better through hole plating and substantial elimination of smear are obtained by employing an immersion tin coating. A novel immersion tin coating is also disclosed.

2. Prior Art

Methods for improving the adhesion of metallic layers to non-conducting surfaces of printed circuit boards in a multilayer board are disclosed by Nielsen et al. U.S. Pat. No. 3,536,546; Luce, et al., in U.S. Pat. No. 3,585,010; Berdan, et al., U.S. Pat. No. 4,260,449 and Torday, et al., U.S. Pat. No. 4,469,567. Nielsen et al., disclose the use of a cyanide based tin immersion coating for improving the adhesion of copper-epoxy glass laminates. Luce, et al., disclose the production of circuit board laminates employing a copper foil conductor treated by electrodepositing a thin metal layer on it. The metal consists of indium, zinc, tin, nickel, cobalt, brass, or bronze. These metals optionally may be deposited on the surface of the copper by vapor deposition.

Immersion tin coatings are disclosed by Orio, et al., British Pat. No. 2,072,709; Shipley, et al., U.S. Pat. No. 3,303,029 and the various references cited in Orio, et al., and Shipley, et al. Shipley et al., disclose the use of hypophosphorous acid stannous sulphate immersion tin compositions.

SUMMARY OF THE INVENTION

The present invention relates to a novel immersion tin composition comprising:

(a) a thiourea compound

(b) a urea compound

(c) a chelating agent

(d) a reducing agent

The invention also relates to a process for improving the adhesion of a metal layer of a printed circuit board to the non-conductive surface of a circuit board comprising coating the metal layer with an immersion tin composition especially the composition of the invention. By eliminating the black copper oxide layers of the prior art as an adhesion promoting layer, better through hole plating is realized.

By coating the metal layers of a multilayer circuit board with an immersion tin composition prior to drilling through holes in the board, smear in the holes is eliminated or substantially eliminated thereby minimizing or eliminating the etch-back treatment of the through-hole. Although the inventors do not wish to be limited by any theory, it is believed that the tin acts as a lubricant and to dissipate heat during the drilling of the holes. The composition of the invention is especially useful for this purpose.

DETAILED DESCRIPTION

The present invention relates to a novel immersion tin composition and its use in the manufacture of printed circuit boards. Printed circuit boards (PCB's) comprise a non-conducting or dielectric base made up of a fibrous material such as glass fibers, paper and the like, impregnated with a resinous material such as an epoxy or phenolic resin. The board is clad with a metal conductive layer such as copper on either one or both surfaces. Multilayer boards (MLB's) comprise several circuit boards laminated to one another by means of an adhesive. In addition to rigid boards (as described above), flexible boards can be produced employing thermoplastic dielectric layer such as fluorocarbon polymers, nylon polymers, polyimides, polyparabanic acids, and polyesters. Production of these types of printed circuit boards are described in Printed Circuits Handbook, Second Edition, edited by C. F. Coombs, Jr. McGraw-Hill, 1979, which is incorporated herein by reference. Laminated combinations of flexible and rigid boards are also finding utility in some more recent applications for MLB's. The present invention applies to all of these structures.

In the manufacture of PCB's, a metal conductive foil such as copper is bonded to the circuit board, although for the purposes of the present invention any metal applied to a non-conductive dielectric circuit board as a foil or by electrodeposition, electroless deposition may be used.

Prior to laminating, the metal surface is treated in an art known manner to produce electrically-conductive lines (circuits) for the transfer of current between components of an electrical circuit, the components comprising by way of example, diodes, transistors, resistors, capacitors, and the like. The circuits may be formed either by a positive or negative working photo resist, silkscreen resist, or hand painted resist process followed by etching and in some instances, electrodeposition of a metal or metals, all of which is known in the art.

The circuits of the inner layers of an MLB are formed by a print and etch process in which a positive working photo resist is applied to the metal layer, a positive circuit image projected onto the resist, followed by a developing process to leave a positive resist pattern. The positive resist pattern can also be formed by a negative working photo resist through which a negative circuit image is projected. The board is then etched after which the positive resist is removed. The elements of the circuit obtained do not have to be electrically connected to one another. These circuit elements that are not connected are placed on the board for subsequent connection to other boards in the MLB array.

In MLB's, the circuit of one board is connected to the circuit of one or more of the other boards in the multilayers. This is achieved by forming pads or circular areas of metal at a point or points on the conductive line or lines of the board. The pads may also be isolated from the conductive lines. The other board or boards that are to be connected are similarly provided with pads and in the laminating process the pads of the different boards are aligned over one another.

In forming MLB's by laminating, a prepreg is inserted between the surfaces of the boards that are to be laminated after which the multiple layers are further treated by applying heat and pressure to them. The prepreg generally comprises a woven or non-woven layer or layers of fibers such as glass, cellulose (e.g. paper), and the like, glass being preferred. The prepreg also is impregnated with a so-called "B-stage" resin such as an epoxy resin that has been partially cured. Art known equivalents of epoxy resins are also employed as adhesives such as acrylic resins (used with polyimide circuit boards) or polyester resins.

The MLB is then pressed and cured with the pads of the circuits of the different boards that are to be connected aligned over one another. After curring, the pads of the MLB's are drilled. The diameter of the drill is considerably less than the diameter of the pad, the ratio of diameters between the pad and the drill being 2:1 or greater so that the overall structure comprises at a minimum a pad from one board aligned over a pad from another board with a hole passing through them. Since the hole in cross-section ideally presents a surface of alternating layers of the pads of the individual PCB's separated by the non-conductive base, an electrically conductive element has to be employed in the hole to form an electrical connection between the pads. This is done by a process known in the art as through hole plating (PTH).

PTH processes are also employed for connecting two metal conductive surfaces having a single non-conductive or dielectric board interposed between them for the formation of a PCB. Boards of this type and the formation of through holes in such boards are also within the scope of the present invention and are intended to be included within the broad definition of the MLB's as that term is used throughout the specification.

Electroless copper is employed as a PTH plating material. Standard electroless copper plating solutions known in the art are used for this purpose. In order to promote the deposition of electroless copper on a non-conductive surface, the non-conductive surface is treated with a stannous chloride sensitizer solution followed by a super sensitizer solution of divalent palladium chloride. The stannous chloride is oxidized to stannic chloride and the palladium chloride reduced to palladium metal. A preferred method is to employ an activator comprising colloidal palladium containing stannic tin. Stannic tin forms a protective colloid around the metallic palladium, and the solution implants a precious metal site on the non-conductive surface for the purpose of initiating the deposition of the copper by chemical reduction. A postactivator is then employed, generally an acid, to solubilize the protective colloid and expose the precious metal, i.e. palladium. The subsequently applied electroless copper coating solution contains a reducing agent such as formaldehyde, and when in the presence of palladium reduces the cupric ions in the solution to copper metal. The copper metal plates out on the surface of the through hole, making electric contact with the walls of the metal pads through which the hole is drilled. The electroless copper may have subsequent metal coatings applied to it by electrolytic means.

Because the outer conductive metal layer of an MLB is formed as part of the PTH process, a print and etch procedure cannot be employed for forming circuits on this layer. The etching step would remove the plating applied in the through hole and would be self-defeating. For this reason, after the PTH process is completed, a negative circuit pattern is formed on the surface of the MLB by means of a negative working photo resist, a positive circuit image projected onto the resist followed by developing. This leaves a negative photo resist circuit pattern on the board with bare metal exposed corresponding to the area of the circuit. The negative resist pattern can also be obtained by a positive working photo resist through which a negative circuit image is projected. The bare metal corresponding to the circuit is then coated by electrolytic means with a second metal that acts as an etch-resist. Tin lead alloys are the most common material used in this respect. The etch resist coating also coats the metal surface applied to the through holes in the PTH process. The photo resist is then removed and the board is etched resulting in the formation of a circuit on the outer layer of the MLB having a tin lead coating on the circuit as well as on the walls of the through hole.

One of the difficulties encountered in the prior art manufacture of MLB's is the low bonding strength sometimes obtained between the prepreg and the metal surface of a circuit board in the array of boards that make up the MLB. These problems are especially prevalent when the metal layer comprises copper. The bonding between the copper clad board and the prepreg was improved by etching the copper with ammonium persulfate; however, only slightly improved bonding strengths were obtained. Some improved adhesion over the etching process was obtained by pumice spraying to micro-etch the copper surface or provide cavities in the copper surface to which the resin such as the epoxy resin of the prepreg could be bonded to. Other mechanical processes such as brushing similarly provided a mechanical alteration of the surface of the copper to improve the bond strength.

Even better bond strengths between the copper layer and the prepreg were obtained with a so-called black oxide coating in which the copper surface of a PCB was treated with a mixture of sodium hypochlorite and sodium hydroxide to produce a black copper oxide. Although better bond strengths were obtained, one of the difficulties with using this method was that the composition of the sodium hypochlorite/sodium hydroxide solution changed over a period of time and erratic results were obtained such as varying thicknesses of the black oxide. The formation of the black oxide coating was time and temperature dependent and as a result the bath employed for the development of the coating had to be closely monitored. Additionally, prior to the formation of the black oxide coating, the copper surface had to be prepared by brushing, rinsing, and etching either with ammoniun persulfate or a sulfuric acid-hydrogen peroxide mixture.

It was subsequently discovered that by lowering the sodium hypochlorite/sodium hydroxide bath temperature from 90°-95° C. to 60°-65° C. some economies could be realized in that less heat had to be supplied to the bath, but more importantly the process was easier to control. By employing temperatures of from about 60°-65° C. a bronze or brown colored copper oxide layer was produced on the surface of the copper and slightly better bond strengths were obtained.

It was essential to control the black oxide formation on the surface of the copper since if the oxide was excessively thick, it would shear readily thereby destroying the bond between the copper metal and the prepreg. Additionally at the proper thickness, the black copper oxide was not sufficiently flexible so that it could not be used in a flexible MLB. Even though the brown or bronze colored copper oxides obtained at the 60°-65° C. bath temperatures were easier to control, these coatings were not without their difficulties. Coating of this type were not readily accepted by the purchasers of MLB's since they were mottled or uneven in color and gave the appearance that the coating was not uniform. This mottled appearance or "brown spotting" has been described as affecting the dielectric properties of the resin, and consequently, the overall performance of the printed circuit (Cf. Berdan, et al., U.S. Pat. No. 4,260,449) as well as a lowering of the peel strength of the copper foil (i.e. bonding strength) to the prepreg (Cf. Torday, et al.; supra, column 1, lines 27-35).

Torday, et al. (supra) and Luce, et al. (supra), describe methods for overcoming some of the difficulties encountered with the bonding of the copper metal to the prepreg by the electrodeposition or vapor deposition of various alloys or metals to the surface of the copper prior to bonding. One of the difficulties with the deposition of a metal film on the copper is that the processes must be closely controlled to assure that proper metal film thicknesses will be obtained. Skilled operators and constant monitoring of the composition and the conditions of deposition are required in order to obtain uniform thicknesses of these metals on copper.

Even with the prior art processes for treating the copper metal surface to obtain better adhesion to the prepreg, the laminating of the individual circuit boards to form the MLB was a time consuming process. In the laminating process, the individual PCB's assembled in an MLB are placed in a press that is heated to 175° C. held there for about 10-15 minutes to bring the MLB array up to temperature after which a pressure of 250-400 psi is applied. The MLB is held at this temperature and this pressure for approximately 45-50 minutes after which heating is stopped and the MLB allowed to cool for about 10-15 minutes while in the press. After this cooling period, the pressure is released and the MLB is removed from the press.

In subsequent operations after providing through holes and PTH connectors, circuit components are placed on the MLB and soldered to the circuits. Two types of soldering methods are employed one of which comprises a hand soldering process the other of which is an automatic soldering method employing a wave soldering apparatus known in the art in which the bottom circuits of the MLB through which leads of circuit components project are contacted for about 60 seconds with a solder wave that is maintained at a temperature of approximately 290° C. MLB's in which the various laminae are not properly bonded to one another at the interfaces of the copper foil and the prepreg will delaminate when exposed to these soldering conditions.

Smearing is another difficultly encountered in the manufacture of MLB's whereby the drill bit employed to form the hole through the aligned pads in an MLB picks up resinous material and deposits this material on the wall of the hole. Since the wall of the hole contains alternating resinous material layers and metal layers, the surface of the metal layers that form part of the hole wall will be coated with the resinous material thereby preventing any metallic plating material applied to the surface of the hole wall from contacting the metal layers and forming an electrically conductive connection with it. It is believed that the resinous material such as a B-stage epoxy resin used in the prepreg comprises the principle material involved in the smearing of the hole. Smearing, therefore, renders the PTH process ineffective.

The problem of smearing is overcome by a process known in the art as "etch-back" in which a strong mineral acid such as sulfuric acid (optionally containing some hydrofluoric acid) is used to etch away the "smear" from the wall of the hole. Hydrofluoric acid is added to the sulfuric acid to remove any glass fibers from the circuit board that might be projecting into the hole. The glass fiber ends come from the glass fiber battings employed in the manufacture of the circuit boards or prepreg and are removed since they cause imperfections in the surface of the metallic coating applied by the PTH process.

One of the difficulties with the etch-back process is that it requires very careful control in order to prevent excessive etching of the wall of the hole. The concentration and temperature of the etching solution has to be carefully controlled and monitored as well as the length of time over which the etching process is conducted. Again, because of these critical conditions, skilled operators are required to perform this process.

Precise control of the degree of etch-back is critical in order to obtain an acceptable metal coating on the wall of the through hole. In some instances in the etch-back process, the etching solution will remove the resinous layer of the MLB preferentially over the metal or copper layers in the hole. This will result, after etching, in the metal layers projecting slightly beyond the wall of the hole as defined by the surface of the resinous material. If this metal layer projection is excessive, the metal coating applied to the wall of the hole by the PTH process will be uneven and will not make proper electrical contact with the metal layers in the hole.

The phenomenon of the metal layer being etched at a faster rate than the resinous layer in the hole is known as "reverse etch" which in some instances presents the same type of problem encountered where the metal layer projects to far into the hole after etching.

Another difficulty encountered in the prior art PTH process is leaching, in which the black copper oxide formed on the copper foil is deposited as a residue in the through hole during the etch-back procedure. Although after the etch-back process is completed the hole is rinsed, the rinsing process is not effective to remove all of the black copper oxide deposited on the wall of the hole. This causes several problems, the first of which is that the black oxide may interfere with the palladium catalyst deposited on the wall of the hole for promoting the electroless deposition of copper in the PTH process. Secondly, because the black oxide is deposited on the wall as a non-adhering particulate composition, it interferes with the bonding of the electroless copper on the surface of the wall of the hole. Thirdly, black oxide diffuses through the PTH coating resulting in pin holes which interfere with the integrity of the coating by providing sites for the coating to be attacked when the MLB is subjected to etching after the PTH process is completed.

The black oxide layer that forms part of the surface of the wall of the through hole not only contributes to these problems but is also etched away in the etch-back process leaving a void in which etching solution components are trapped. These components are not always removed in the rinsing step and as a result also interfere with the PTH meal layer applied to the through hole.

Blow holes may also form in the PTH coating by the different thermal coefficients of expansion of the black oxide and the glass material employed in the construction of the circuit boards. The blow holes occur when the board is submitted to extremes of temperature either during the soldering operation or when the boards is in use. Extremes in temperature are also encountered in the through hole after electroless plating of copper when a second metal coating is applied to the PTH process comprising a tin-lead layer that acts as an etch resist. The tin-lead coating is applied electrolytically and subsequently heated or flowed in order to produce a tin-lead coating in the through hole having greater integrity. Pin holes and blow holes in the PTH coating can be the cause of reduced conductivity in the PTH and are to be avoided for this reason.

The use of immersion tin coatings for plating metal surfaces is known. This process does not employ an electric current but is based on an electrochemical displacement reaction. The metal substrate that is to be plated generally is more active (less noble) than the metal salt that is dissolved in the coating composition or plating solution. Copper may be plated by a tin solution even though copper is more noble than tin when the immersion coating composition is acidic and contains thiourea as a so-called "complexing" agent. It has been theorized that the relative electrode potentials of tin and copper are reversed in the presence of an appropriate Cu⁺ "complexing agent." Once the metal substrate is completely coated, it is no longer available to displace the metal ions in the immersion coating composition.

Some of the limitations of the immersion coating processes were the slow plating speeds, limited thickness of the coating, a well as the extensive degreasing, cleaning and oxide removal of pre-coating steps that had to be employed.

The immersion coatings were also porous. The problems of porosity were attempted to be overcome by greater coating thicknesses. Additionally, high coating temperatures (about 82°-85° C.) had to be employed which in some instances caused noxious fumes to be produced from the coating solution and prevented the use of some low cost plastic materials of construction for the plating tank.

Coating times of from 10 to 40 minutes were not uncommon for this process. These times were employed in order to obtain nonporous, relatively thick films on the metal substrate. Additionally, the metal substrate such as a copper substrate employed in circuit boards had to be grease free and oxide free in order to obtain relatively thick tin coatings of 80 millionths of an inch thick after about 40 minutes. (Cf. Shneble, Jr., U.S. Pat. No. 3,917,486).

It is, therefore, an object of the present invention to overcome these and other difficulties encountered in the prior art.

A further object of the present invention is to provide a composition for the treatment of the surface of metal conductive layers of a circuit board and especially a copper layer to promote the adhesion of the metal to a non-conductive surface.

It is a further object of the present invention to provide a process for improving the bond strength between the conductive surfaces and the non-conductive or dielectric layers of an MLB assembly.

It is also an object of the present invention to provide a composition for treating the metal surfaces of a circuit board to be employed in the fabrication of an MLB that will significantly reduce the time and/or laminating temperature used in forming the MLB while maintaining or increasing the bond strength between the layers of an MLB.

It is also an object of the present invention to provide a process for treating the metal surfaces of a circuit board to be employed in the fabrication of an MLB that will significantly reduce the time and/or laminating temperature used in forming the MLB while maintaining or increasing the bond strength between the layers of an MLB.

It is the further object of the present invention to provide a novel composition for reducing or eliminating smearing in an MLB.

It is the further object of the present invention to provide a novel process for reducing or eliminating smearing in an MLB.

It is the further object of the present invention to provide a novel immersion coating composition.

It is the further object of the present invention to provide an adhesion promoting flexible metal coating on the metal surface of a circuit board used in an MLB.

It is also an object of the present invention to provide a novel composition which may be employed in the production of metal immersion coatings.

It is also an object of the present invention to provide an immersion coating that may be applied to a metal surface that is oxidized or partially oxidized.

It is a further object of the invention to provide a novel immersion tin coating composition that simultaneously cleans and coats a metal substrate to which it is applied.

It is a further object of the present invention to provide a novel metal immersion composition that may be employed as a coating composition at room temperatures.

It is the further object of the present invention to provide such an immersion composition that may be employed as a coating material that will deposit a uniform, non-porous coating from about 0.08 to about 0.17 microns.

It is also an object of the invention to provide such a composition that will form a coating in about 90 seconds.

It is also an object of the present invention to provide sulfur containing immersion coating component compositions that do not generate intolerable levels of hydrogen sulfide during the storage of the same.

It is also an object of the present invention to provide tin sulfate containing immersion coating compositions that provide significant improvements over prior art tin chloride based immersion coating compositions.

It is also an object of the present invention to provide tin salt based immersion coating compositions that do not precipitate out any significant levels of tin compounds when stored at ambient temperatures for several months or longer.

These and other objects have been achieved according to the present invention which relates to an immersion composition, especially an immersion tin composition comprising:

    ______________________________________                                         (1-a)        (a)   a thiourea compound                                                      (b)   a urea compound                                                          (c)   a tin salt                                                  ______________________________________                                    

The composition may optionally contain:

    ______________________________________                                         (1-b)        (d)   An optional chelating agent                                              (e)   a reducing agent and                                                     (f)   an acid                                                     ______________________________________                                    

The acid is employed to maintain an acid pH. The reducing agent prevents or minimizes any oxidation reactions whereby the tin salt which is preferably a stannous salt could be oxidized to its higher valent form i.e., a stannic salt. Preferred compositions comprise those employing components (a) through (f) as listed above and those optionally containing (1-c) the salt of another metal (as noted herein) and (1-d) a surfactant.

It has also been found that the aforesaid composition can be employed as a coating composition to improve the adhesion of a metal substrate of a PCB to a non-conductive surface of a circuit board and also eliminates, substantially eliminates or minimizes smearing when through holes are drilled in an MLB. Other immersion tin compositions can be employed in this aspect of the invention e.g. such as those disclosed in the U.S. Pat. Nos. to Shipley, 3,303,029; Ceresa, et al., 2,891,871; Sullivan, et al., 2,369,620; and Bradley, 2,282,511.

By employing an immersion tin composition and especially the composition of the present invention in the manufacture of an MLB, problems of pin holes and blow holes are eliminated, or substantially eliminated in the PTH coating.

The essential feature of the composition of the present invention is the use of the combination of a thiourea compound and a urea compound in an immersion coating. It has been found that when using this combination that bright, uniform, non-porous thin coatings of tin or tin alloys can be applied to a metal substrate at a faster plating rate and a purer coating obtained. Tin or tin alloy coatings from about 0.08 to about 0.17 microns are obtained that have good solderability and are good etch-resists because they are substantially non-porous.

The combination of the thiourea compound and urea compound allow coating of metal substrates with substantially no pre-cleaning or minimal pre-cleaning. The composition of the invention acts as a cleaning composition to some degree and in many instances can be applied directly on to a metal substrate without pre-cleaning.

Thus the novel tin immersion coating comprising the combination of the thiourea composition and urea composition has been found to act as a cleaner and degreaser for the metal substrate over which the coating is applied. Extensive oil and/or grease removal and a scrubbing of the metal substrate to remove metal oxides is either substantially reduced or eliminated. The coating composition will deposit a tin layer on a metal oxide surface such as copper oxide.

The components of the composition are present in the following amounts on a molar basis:

    ______________________________________                                         (2-a)  (a)   about 10 to about 125 parts of a thiourea                                      compound                                                                 (b)   about 10 to about 125 parts of a urea compound                           (c)   about 1 to about 15 parts of a tin salt.                          ______________________________________                                    

where the composition optionally contains a chelating agent, a reducing agent and an acid, these components are present in the following amounts on a molar basis:

    ______________________________________                                         (2-b)  (d)   0 to about 40 and particularly about 5 to                                      about 40 parts of a chelating agent.                                     (e)   about 5 to about 110 parts of a reducing agent                           (f)   0 to about 250 parts of an acid.                                  ______________________________________                                    

The composition optionally may contain the salt of a second metal in the following amounts, on a molar basis:

    ______________________________________                                         (2-c)                                                                               (g)    about 0.2 to about 55 parts of a salt of a                                     Group VIII metal, a Group IVA metal (with the                                  exception of tin) a Group IIB metal and Group IB                               metal.                                                             ______________________________________                                    

When the reducing agent is an acid such as H₃ PO₂ additional acid (component (f)) does not have to be present.

A surfactant (2-d) may also be added to the composition in an amount as indicated herein.

In one aspect of the invention a composition is provided comprising;

    ______________________________________                                         (3-a)       Thiourea      10-100  g/l                                                      Urea          5-80    g/l                                                      Tartaric Acid 5-80    g/l                                                      Glucose       5-80    g/l                                                      H.sub.2 SO.sub.4 (36N)                                                                       2-60    ml/l                                                     SnSO.sub.4    1-30    g/l                                          ______________________________________                                    

Similarly where a combination of tin and another metal is to be coated such as nickel the composition will have the following components added to it:

    ______________________________________                                         (3-b)       Triton X-100  0.5-10  ml/l                                                     NiSO.sub.4    5-80    g/l.                                         ______________________________________                                    

In one embodiment, a coating composition is prepared comprising the following:

    ______________________________________                                         (4)      Thiourea         60       g/l                                                  Urea             40       g/l                                                  Tartaric Acid    40       g/l                                                  Glucose          40       g/l                                                  H.sub.2 SO.sub.4 (36N)                                                                          30       ml/l                                                 SnSO.sub.4       20       g/l                                                  Triton X-100 (1) (optional)                                                                     5        ml/l                                                 NiSO.sub.4 (optional)                                                                           40       g/l                                                Water          balance                                                  ______________________________________                                    

The various equivalents as set forth herein for the foregoing components of formulas (1-a) through (1-d); (2-a) through (2-d); (3-a) and (3-b); and as known in the art may be substituted for such components on an equimolar basis.

Various combinations of tin and other metals may be used in the composition as soluble salts e.g. water soluble salts based on mineral acid or organic acid salts of these metals. The metals that may be used with tin include the soluble e.g. water soluble salts of a metal taken from Group VIII, Group IB, Group IIB and Group IVA (with the exception of tin) of The Periodic Table of the Elements and mixtures thereof. Thus, in addition to tin nickel, tin lead or tin mercury coatings, may be deposited by means of the immersion composition of the invention.

Additionally, other immersion compositions, useful for plating metal surfaces are prepared by substituting other soluble, e.g., water soluble metal salts for tin of formulas (1-a) through (1-d); (2-a) through (2-d); (3-a) and (3-b); and (4), these other metal salts comprising those based on the metals of Group IVA; VB; VIB; VIIB; IB; IIB and IIIA of the Periodic Table of the Elements; the group IVA, VIII, IB, IIB and IIIA metals being preferred; and the Group IVA, VIII and IB metals being especially preferred. As referred to in the immediately preceding description, the Group IVA metals are intended to include the Group IVA metals with the exception of tin. The anions of these metal salts are the same as those defined herein for the tin salts. Additionally, the metal salts as defined above and herein are preferably employed in their lowest oxidation states e.g.,

Sn(2); Ni(2); Hg(1); Au(1) and the like. Various mixtures of these other metal salts may also be employed. Salts of lead, mercury, silver, indium, gold and palladium are especially suitable.

The tin coating compositions of the invention are useful as an etch resist in lieu of electrolytic tin lead etch resists used in the manufacture of an MLB as described herein.

The foregoing tin immersion coating provides many advantages over the coatings employed in the prior art especially the tin immersion coatings of the prior art. Thinner pore free coatings are obtained i.e. coatings of about 0.08 to about 0.175 microns compared to the prior art in which 1-2 micron coatings (40-80 millionths of an inch) are utilized to obtain pore free coatings.

The composition of the present invention will produce coatings of from about 0.001 to about 0.25 microns and especially from about 0.05 to about 0.175 microns. The coating times will vary from any where between about 2 seconds up to 5 minutes (especially 5 seconds to about 120 seconds), suitable coatings (about 0.065 microns) being obtained at about 30 seconds. The coating temperatures may vary any where from about 0° to about 30° C., especially from about 15° to about 30° C. although higher temperatures may also be employed.

Excellent adhesion of the inner layers of an MLB are obtained when the metal surfaces of the inner layers are coated with the immersion tin coating of the present invention prior to laminating. No delamination of an MLB prepared in such a manner was noted after exposure of the MLB to a temperature of 290° C. for 10-60 seconds.

In addition to eliminating or substantially eliminating smearing in the through hole of an MLB, by acting as a lubricant for the drill bit as well as a heat dissipating material, the immersion tin coating of the invention also reduces the bonding times and/or temperatures employed in making the MLB. Typically, by coating the inner layers of an MLB prior to laminating with the tin immersion coating, the preheat step in the MLB laminating process may be eliminated and the laminating time reduced to about 20 to about 30 minutes from the standard 45 minute cycle ordinarily required for this step. Pin holes and blow holes in PTH coatings are also substantially eliminated or minimized when employing the coating to promote adhesion of a prepreg to a metal layer in an MLB.

Because the immersion tin coating layer is used in lieu of a black copper oxide layer to promote adhesion to the prepreg, excessive etching of the adhesion-promoting layer is avoided with all of the problems associated with it in the etch-back and PTH processes. The immersion tin layer is substantially unaffected in an etch-back process as compared to the back oxide layer.

The thiourea compounds and urea compounds of the present invention may be represented by the formula:

    (C)(X)(N).sub.2 (R.sup.1).sub.a (R.sup.2).sub.a (R.sup.3).sub.a (R.sup.4).sub.a

where

R¹ =

(1) H

(2) alkyl or alkenyl having up to about 6 carbon atoms

(3) aryl, aralkyl, or alkaryl having up to about 12 carbon atoms

(4) cycloalkyl, cycloalkylalkyl, or alkylcycloalkyl having up to about 12 carbon atoms

(5) R⁵ (CO) where R⁵ may be the same as radicals (2) through (4) as defined above for R¹

(6) CH₂ OH

(7) (C) (X) (N)₂ (R¹)_(a) (R²)_(a) (CO)₂

(8) (C) (X) (N)₂ R¹ R² R³

(9) (C) (X) (N) R¹ R²

(10) (C) (X) (N)₂ R¹ R² (CO)

R², R³ and R⁴ may be the same as radicals (1) through (6) as defined above for R¹.

a=1 or 0

For the thiourea compounds and their analogs employed according to the present invention X=S, Se or Te; X preferably is S.

For the urea compounds employed according to the present invention, X=oxygen.

Mineral acid salts of the thiourea and urea compounds may also be used.

The thiourea compound of the present invention comprises either thiourea or the various art known derivatives, homologs, or analogs thereof. Compounds that may be employed in this respect comprise 2,4-dithiobiuret; 2,4,6-trithiotriuret; alkoxy ethers of isothiourea; thiocyanuric acid (trimer of thiourea); thioammelide (trimer of thiourea); monalkyl or dialkyl thiourea, where the alkyl group comprises a lower alkyl group, having up to about four carbon atoms such as diethyl thiourea or monoethyl thiourea; saturated or unsaturated cyclic hydrocarbons mono- or disubstituted thioureas such as naphthyl thiourea, diphenyl thiourea, cyclohexyl thiourea and the like, where the cyclic hydrocarbons has up to about ten carbon atoms; the disulfide of thiourea; thio-imidol (the reaction product of thiourea and sodium hydroxide); thiocarbamic acid esters (the reaction products of thiourea and an alcohol comprising ROH where R is a saturated or unsaturated aliphatic or cyclic group having up to about ten carbon atoms) the oligomers of thiourea and formaldehyde, e.g. monomethylol, dimethylol, and trimethylol thioureas; S-alkyl pseudo thioureas (manufactured by the reaction of thiourea with an iodo lower alkane such as iodo methane where the lower alkyl group contains up to about five carbon atoms); thiocarbonic acid esters of thiourea and R.sup. 5 OH, (R⁵ as defined above) especially where R⁵ is lower alkyl; thioureadioxide (aka formamidinesulfinic acid [1758-73-2, C.A. Reg. No.]); the reaction product of a saturated or unsaturated aliphatic or cyclic organic acid having up to about 12 carbon atoms and especially the lower aliphatic monocarboxylic acid reaction products with thiourea e.g. acylthioureas, and the mineral acid salts of thiourea e.g. thiourea mono- or di-sulfate.

Similarly, the urea compound comprises either urea or the various substituted ureas or urea reaction products such as biuret; monoalkyl or dialkyl urea, where the alkyl group comprises a lower alkyl group having up to about four carbon atoms such as diethyl urea or monoethyl urea; saturated or unsaturated cyclic hydrocarbon mono- or disubstituted ureas where the cyclic hydrocarbon has up to ten carbon atoms, such as naphthyl urea, diphenyl urea, cyclohexyl urea and the like; alkoxy ethers of iso-urea especially lower alkoxy ethers of iso-urea where the lower alkyl group contains up to about five carbon atoms, these products being manufactured by the reaction of a lower alkanol with cyanamide hydrochloride; acid derivatives of urea in which the hydrogen atom of urea is substituted by an acyl group, these compounds sometimes being referred to as ureides obtained by the reaction of urea with a monocarboxylic aliphatic saturated or unsaturated organic acid having to about 20 carbon atoms and especially those acids having up to about four carbon atoms; the mineral acid salts of urea e.g. urea mono- or disulfate; triuret; cyanuric acid (a trimer of urea); ammelide (a trimer of urea); imidol; carbamic acid esters of urea and R⁵ OH, (where R⁵ is defined above) especially alkyl carbamates made by the reaction product of an organic alcohol with urea especially an alkanol such as a lower alkanol containing up to about four carbon atoms; monomethylol urea, dimethylol urea, trimethylol urea and other oligomers of urea and formaldehyde. The various substituted ureas and their use in immersion coatings is further disclosed by Ceresa, et al., in U.S. Pat. No. 2,891,871 which is incorporated herein by reference.

Other urea and thiourea compounds that may be employed comprise:

urea nitrate;

urea oxalate;

urea phosphate;

urea sulfate;

1-acetylurea;

1-acetyl-3-methylurea;

1-acetyl-2-thiourea;

S-acetyl-2-thiourea-hydrochloride;

1-allylurea;

1-allyl-3-phenylurea;

1-allyl-2-thiourea;

1-(4-aminobenzenesulfonyl)urea;

1-(4-aminobenzenesulfonyl)-2-thiourea;

1-benzoylurea;

1-benzoyl-2-thiourea;

1-benzylurea;

1-benzyl-2-thiourea;

1,3-bis(2-ethoxyphenyl)urea;

1,3-bis(4-ethoxyphenyl)urea;

1,3-bis(2-4-dinitrophenyl)urea;

1-3-bis-(hydroxymethyl)urea;

1,3-bis(1-hydroxy-2,2,2-trichloroethyl)urea;

1(2-bromo-2-ethylbutanoyl)urea;

1(2-bromo-3-methylbutanoyl)urea;

1(2-bromophenyl)urea;

1(3-bromophenyl)urea;

1(4-bromophenyl)urea;

1-butylurea;

1-sec-butylurea;

1-tert-butylurea;

1-butyl-3-phenyl-2-thiourea;

1(2-chlorophenyl)urea;

3(4-chlorophenyl)-1,1-dimethylurea;

1(2-chlorophenyl)-2-thiourea;

1(4-chlorophenyl)-2-thiourea;

1,3-diacetylurea;

1,1-diethylurea;

1,3-diethylurea;

1,3-diethyl-1,3-diphenylurea;

1,3-diethyl-1,3-diphenyl-2-thiourea;

1,3-diethyl-2-thiourea;

1,1-dimethylurea;

1,3-dimethylurea;

1,3-dimethyl-1,3-diphenylurea;

1,3-dimethyl-2-thiourea;

1,1-di(2-naphthyl)urea;

1,3-di(1-naphthyl)urea;

1,3-di(2-naphthyl)urea;

1,3-di(1-naphthyl)-2-thiourea;

1,3-di(2-naphthyl)-2-thiourea;

1,1-diphenylurea;

1,3-diphenylurea;

1,3-diphenyl-1-methylurea;

1,3-diphenyl-S-methyl-2-thiourea;

1,1-diphenyl-2-thiourea;

1,3-diphenyl-2-thiourea;

1,1-dipropyl-2-thiourea;

1,3-dipropyl-2-thiourea;

1,3-diisopropyl-2-thiourea;

1,3-di(2-tolyl)-2-thiourea;

1,3-di(4-tolyl)-2-thiourea;

1(3-ethoxyphenyl)urea;

1(4-ethoxyphenyl)urea;

1-ethylurea;

1-ethyl-1-phenylurea;

1-ethyl-3-phenylurea;

1-ethyl-3-phenyl-2-thiourea;

1-ethyl-2-selenourea;

1-ethyl-2-tellurourea;

1-ethylidene-2-thiourea;

1-hydroxyurea;

1(hydroxymethyl)urea;

1(2-iodo-3-methylbutanoyl)urea;

isobutylurea;

1(2-isopropyl-4-pentenoyl)urea;

1(4-methoxy-phenyl)urea;

1-methylurea;

1(2-methyl-2-butyl)urea;

1(3-methyl-butyl)urea;

1-methyl-3(1-naphthyl)-2-thiourea;

1-methyl-1-nitrosourea;

1-methyl-3-phenyl-2-thiourea;

S-methyl-2-thiourea;

S-methylisothiouronium iodide;

S-methylisothouronium nitrate;

S-methylisothiouronium sulfate;

1-methyl-2-thiourea;

1(1-naphthyl)urea;

1(2-naphthyl)urea;

1(1-naphthyl)-3-phenyl-2-thiourea;

1(1-naphthyl)-2-thiourea;

1(2-naphthyl)-2-thiourea;

1-nitrourea;

1-oxalylurea;

1(2-phenoxy-ethyl)urea;

1-phenylurea;

1(phenyl-acetyl)urea;

1-phenyl-2-thiourea;

S-phenyl-2-thiourea;

1-propylurea;

2-selenourea;

2-tellurourea;

1(sulfonamylphenyl)urea;

1,1,3,3-tetraethylurea;

1,1,3,3-tetramethylurea;

1,1,3,3-tetramethyl-2-thiourea;

1,1,3,3-tetraphenylurea;

1,1,3,3-tetraphenyl-2-thiourea;

2-thio-1(2-tolyl)urea;

2-thio-1(3-tolyl)urea;

2-thio-1(4-tolyl)urea;

2-thio-1,1,3-trimethylurea;

2-thio-1,1,3-triphenylurea;

1(2-tolyl)urea;

1(3-tolyl)urea;

1(4-tolyl)urea;

1,1,3-trimethylurea;

Some especially preferred thiourea compounds in addition to thiourea that may be employed according to the invention comprise:

phenylthiourea;

naphthylthiourea;

thiourea disulfide;

oligomers of thiourea and formaldehyde;

N-allylthiourea;

N-mono-p-tolylthiourea (and the equivalents thereof disclosed in U.S. Pat. No. 4,502,927, incorporated herein by reference);

N-alkylthioureas such as methylthiourea (and the equivalents thereof disclosed in West German Pat. No. 3,110,478, incorporated herein by reference);

monophenylthiourea;

metaphenylenedithiourea;

N,N'-ethylenethiourea;

N,N'-dibutyneylthiourea;

N,N'-dibutenylthiourea;

trifluoro acetylthiourea;

isothiourea-S-propionic acid;

amino substituted thioureas such as thio semicarbazide and 1-phenylthiosemicarbazide;

1-aryl-thioureas where the aryl group is phenyl, benzyl or naphthyl;

When substituted urea and thiourea compounds are employed in lieu of urea and thiourea it is preferred that each contain the same substituent. By way of example, if diethylthiourea is used in the composition in lieu of thiourea, diethylurea would be substituted for urea and so forth.

The tin salt of the composition preferably comprises a stannous salt. Although stannous salts of an inorganic (mineral) acid or organic acid may be used according to the invention (e.g. stannous formate, stannous acetate and the like) the tin salt of the present invention may comprise a stannous salt of a mineral acid such as the sulfur, phosphorous, and halogen acids, especially the sulfur acids such as sulfuric acid or sulfamic acid. Alkali metal stannates may also be used such as sodium or potassium stannate and the art known equivalents thereof. In one embodiment of the invention stannous sulfate, stannous sulfamate or stannous acetate is used as the tin salt. Where tin lead coatings are deposited, lead acetate may be used as the lead salt.

The acids that are employed according to the invention may be organic acids or inorganic acids (mineral acids) based on sulfur, phosphorus, or the halogens, the sulfur based mineral acids being preferred such as sulfuric acid or sulfamic acid. Some of the organic acids that may be employed according to the invention comprise monocarboxylic or dicarboxylic acids having up to about six carbon atoms such as formic acid, acetic acid, malic acid, maleic acid, and the like.

It is preferred, if possible not to use halogen acids or halogen salts since halide residues will be produced in the metal coating deposited, these salts interfering with the electrical properties of the metal and may also act as corrosive materials in the coating.

The chelating agents that may be employed generally comprise the various classes of chelating agents and specific compounds disclosed in Kirk-Othmer, Encyclopedia of Chemical Technology, Third Edition volume 5, pages 339-368 incorporated herein by reference. Chelating agents that are especially preferred comprise the aminocarboxylic acids and the hydroxycarboxylic acids. Some specific aminocarboxylic acids that may be employed in this respect comprise ethylenediaminetetraacetic acid, hydroxyethylethylenediaminetriacetic acid, nitrilotriacetic acid, N-dihydroxyethylglycine, and ethylenebis(hydroxyphenylglycine). Hydroxy carboxylic acids that may be employed comprise tartaric acid, citric acid, gluconic acid and 5-sulfosalicylic acid.

The various reducing agents that may be employed according to the present invention are well known in the art and generally comprise reducing acids such as hypophosphorous acid, organic aldehydes whether saturated or unsaturated, aliphatic or cyclic, having up to about ten carbon atoms. Lower alkyl aldehydes having up to about six carbon atoms may be employed in this respect such as formaldehyde acetaldehyde, propionaldehyde, butyraldehyde, and the like. Glucose and reducing acids such as hypophosphorous acid tend to act to prevent oxidation of the metal salts to a higher oxidation state (e.g., SnII to SnIV). Glucose also is a chelating agent and is especially useful for this reason.

The surfactants that may be employed comprise any non-ionic, anionic, cationic or amphoteric surfactant such as those listed in Kirk-Othmer, Encyclopedia of Chemical Technology, Third Edition, Volume 22, pp. 332-387 which is incorporated herein by reference. The non-ionic surfactants are especially preferred.

It has been found that where thiourea, urea, acid and stannous sulfate are admixed together in water to form an immersion coating solution and allowed to stand, at 20±5° C., or at higher temperatures, hydrogen sulfide forms. In order to offset this storage problem this type of immersion coating composition is preferably freshly made up, just prior to use, form a two part system.

Part one of such two part system comprises the thiourea and the urea. The second part of such two part system comprises the tin salt, hypophosphorous acid and, optionally, another acid. Where used, the metal salt, reducing agent and acid and the optionally chelating agent would be added to the part containing the thiourea and urea. These two part compositions could then each be formed as solutions in about 0.5 liters of distilled water and then admixed in approximately equal volumes to form a one liter immersion coating solution. Immersion coating solutions of larger or smaller volume can be made, obviously, by using proportionally larger or smaller volumes of each of the two precursor parts thereof.

A preferred part one solution could then contain

thiourea: 60 grams

urea: 40 grams

distilled water: to 0.5 liter

A preferred part two solution could then contain

concentrated sulfuric acid: 100 ml

hypophosphorous acid (50%): 40 ml

stannous sulfate: 20 gm

distilled water: to 0.5 liter

These two part compositions have H₂ S off-gas levels, upon standing at 20±5° C. for about one day, of about 0 to 5 ppm as compared to H₂ S off gas levels of about 200 ppm for the entire tin immersion coating solution under the same conditions.

The tin immersion coating compositions produced from the two component system provide minimum coating yields of 150 square feet/gallon (100% copper surface) of immersion tin solution. Instron bond strengths (to epoxy pre-preg) obtained with tin immersion coatings formed from such two component systems measure about 3.5 to 5.3 lbs/inch which is comparable to or better than that obtained with a commercially available brown oxide bonding agent.

Where copper substrates as are used in multilayer circuits are immersed, at 30° C., in one liter of the above described tin immersion coating composition made from the two part precursor system, and containing hypophosphorous acid, the following coating thickness of tin were obtained over the following periods of immersion time:

    ______________________________________                                         coating time (seconds)                                                                        coating thickness (microns)                                     ______________________________________                                          45            0.0591                                                           90            0.0875                                                          180            0.1242                                                          600            0.2839                                                          ______________________________________                                    

When this same immersion bath was used at 60° C., a tin coating of 0.5914 microns was obtained on the copper substrate after 6 minutes immersion time. The levels of coated tin were ascertained by dissolving the coated tin from the Cu substrate and calculating the level of thickness based on the amount of tin in the solution determined by ICP analysis.

The following additional examples are also merely illustrative of the present invention.

EXAMPLE 1 Sulfate Versus Chloride Based Baths

Several immersion tin compositions were prepared as summarized in Table 1 below. These were either SnSO₄ /H₂ SO₄ based systems or the corresponding SnCl₂ /HCl based systems. Corresponding compositions were prepared with and without urea.

Small coupons (1.5×0.5 inches) of copper laminate were tin coated using these immersion tin baths. The coating was done at 30° C. for 90 seconds immersion using the sulfate-based baths. The coating was done at 55° C. for 90 seconds immersion using the chloride-based baths. The latter baths must be operated at higher temperatures to prevent percipitation and keep all bath components in solution. Even at this higher temperature, baths 7 and 8 contained much precipitates. Coating with these baths 7 and 8 was done with the precipitate present in what appeared to be an emulsified suspension. After coating, each coupon was thoroughly rinsed in tap water and then deionized water and then air dried. The coupons were visually examined and analyzed by scanning electron microscopy (SEM) for surface morphology.

Results from the above experiment were striking. Coatings from the sulfate-based baths were shiny and uniform in appearance. Those from the chloride-based baths were dull and rather nonuniform in appearance, particularly with short immersion times. SEM analysis confirmed additional key differences. The sulfate-based coatings had a uniform coating morphology which carefully reproduced the topography of the surface. Such surface reproduction was not observed with the chloride-based coatings which were pitted and spongy.

Peel strengths of laminate samples prepared with tin coatings from each of the above baths were determined. The laminates were prepared in the following manner. A strip (˜3×8 inches) of 1 oz. rolled-annealed (RA) copper was coated in a given bath for 90 seconds at either 30° C. for the sulfate-based baths or 55° C. for the chloride-based baths. The coated sample was rinsed thoroughly with water and air dried. It was then used to prepare a laminate sample consisting of the tin-coated copper strip laminated to 4 sheets of prepreg and a glass-epoxy baseboard. All strips were laminated at the same time as part of a larger laminate sample of dimensions of 12×16 inches.

Press conditions for this lamination were:

Start at 30 tons pressure at ambient temperature.

Raise temperature to 345° F. over 20-25 minutes.

At 345° F., raise pressure to 90 tons and temperature to 375° F.

Keep press at 90 tons, 375° F. for 45 minutes.

Cool to ambient temperature and then release pressure.

Peel strengths for the peeling apart of the tin-coated copper for the prepreg/epoxy base were measured on an Instron unit equipped with a 90° constant angle peel test accessory. Results are summarized in Table 2 below. It is seen that peel strengths for the sulfate-based tin coatings are significantly higher than for all of the corresponding chloride-based coatings.

Use of a sulfate-based immersion tin is an improvement over prior art based on chloride systems in that better coatings with higher bond strengths are attainable. Control is significantly easier and the process latitude is wider, particularly with regard to time/temperature. Thin, nonporous, and uniform tin coatings are possible with the sulfate-based system but not with the chloride-based system.

                  TABLE 1                                                          ______________________________________                                         IMMERSION TIN BATHS                                                            ______________________________________                                         Number 1                                                                       Water                  600    ml                                               Conc. Sulfuric Acid    200    ml                                               Thiourea               80     g                                                Urea                   40     g                                                Sodium Hypophosphite   40     g                                                Stannous Sulfate       20     g                                                Water                  To 1   liter                                            Number 2                                                                       Water                  640    ml                                               Conc. Sulfuric Acid    200    ml                                               Thiourea               80     g                                                Urea                   0      g                                                Sodium Hypophosphite   40     g                                                Stannous Sulfate       20     g                                                Water                  to 1   liter                                            Number 3                                                                       Thiourea               60     g                                                Urea                   40     g                                                Tartaric Acid          30     g                                                Glucose                40     g                                                Conc. Sulfuric Acid    20     ml                                               Stannous Sulfate       60     g                                                Triton X-100           20     g                                                Water                  To 1   liter                                            Number 4                                                                       Thiourea               60     g                                                Urea                   0      g                                                Tartaric Acid          30     g                                                Glucose                40     g                                                Conc. Sulfuric Acid    20     ml                                               Stannous Sulfate       60     g                                                Triton X-100           20     g                                                Water                  To 1   liter                                            Number 5                                                                       Water                  507    ml                                               Conc. Hydrochloric Acid                                                                               293    ml                                               Thiourea               80     g                                                Urea                   40     g                                                Sodium Hypophosphite   40     g                                                Stannous Chloride      21     g                                                (dihydrate)                                                                    Number 6                                                                       Water                  547    ml                                               Conc. Hydrochloric Acid                                                                               293    ml                                               Thiourea               80     g                                                Urea                   0      g                                                Sodium Hypophosphite   40     g                                                Stannous Chloride      21     g                                                (dihydrate)                                                                    Number 7                                                                       Thiourea               60     g                                                Urea                   40     g                                                Tartaric Acid          30     g                                                Glucose                40     g                                                Conc. Hydrochloric Acid                                                                               29.3   ml                                               Stannous Chloride      63     g                                                (dihydrate)                                                                    water                  to 1   liter                                            Number 8                                                                       Thiourea               60     g                                                Urea                   0      g                                                Tartaric Acid          30     g                                                Glucose                40     g                                                Conc. Hydrochloric Acid                                                                               29.3   ml                                               Stannous Chloride      63     g                                                (dihydrate)                                                                    water                  to 1   liter                                            Number 8                                                                       Thiourea               60     g                                                Urea                   0      g                                                Tartaric Acid          30     g                                                Glucose                40     g                                                Conc. Hydrochloric Acid                                                                               29.3   ml                                               Stannous Chloride      63     g                                                (dihydrate)                                                                    Water                  To 1   liter                                            ______________________________________                                    

                  TABLE 2                                                          ______________________________________                                         Sulfate Versus Chloride Based Baths for Coating                                                              Laminate                                                                       Peel Strength                                    Bath Number                                                                             Description          (lb/in)                                          ______________________________________                                         1        Sulfate/hypophosphite formula                                                                       4.6                                                       with urea                                                             2        Sulfate/hypophosphite formula                                                                       4.6-4.9                                                   without urea                                                          3        Sulfate formula with urea                                                                           4.4                                              4        Sulfate formula without urea                                                                        4.0                                              5        Cl/hypophosphite based formula                                                                      2.6                                                       with urea                                                             6        Cl/hypophosphite based formula                                                                      2.6                                                       w/o urea                                                              7        Cl-based formula with urea                                                                          2                                                8        Cl-based formula without urea                                                                       3                                                ______________________________________                                    

EXAMPLE 2 Effects of Urea/Hypophosphite In Sulfate-Based Immersion Tins

The effects of urea and hypophosphite (acid or salt) on the properties of several immersion tin compositions were examined. Results are summarized in Table 3 below. Exact compositions are provided in Table 4 below.

Tin coatings on small copper laminate coupons were prepared as in Example 1 at 30° C. and 90 seconds immersion. Samples G-L of Table 3 were analyzed by EDXA (Energy Dispersive X-Ray Analysis) and SEM (Scanning Electron Microscopy).

Strips of 1 oz. copper were coated and laminated as described in Example 1 using immersion tin formulations A-D and G-L in Table 3. Peel strength measurements were made as described in Example 1.

Hydrogen sulfide off-gas levels were determined for these solutions. Each solution was allowed to equilibrate at ambient temperature overnight in a closed bottle that is half filled with immersion tin solution. Draeger tubes were used to measure the hydrogen sulfide level in each bottle upon equilibration.

Some key findings were:

Hypophosphite is effective in preventing precipitate formation.

An x-ray analysis (EDXA) of immersion tin coatings G-L showed some key effects due to the presence of urea. Coatings G-I with urea contained more tin (higher wt.% of tin) and were more pure than corresponding coatings J-L which were made without urea. Tin deposition rate with urea present was approximately 43-55% greater than without the presence of urea. Coatings made with urea present were pure while those made without the presence of urea contained substantial carbon and oxygen.

Lowering the level of hypophosphite in the solution gave lower hydrogen sulfide off-gas levels. Hypophosphorous acid was better than sodium hypophosphite in giving lower off-gas levels.

All formulations in Table 3 afforded coatings on copper that visually, to the naked eye, appeared uniform and shiny (on the shiny side of the 1 oz copper coupons). This included coatings G-L which were also shown essentially equivalent morphologically as determined by SEM analysis.

Instron bond strengths of laminates derived from these tin coatings are consistently uniform within experimental error and lie in the range of 3.8-5 lb/in. Such bond strengths are essentially equivalent to or higher than the value of up to 3.5 lb/in that was measured for a leading brown oxide.

The above results demonstrate the utility of urea as part of an improved immersion tin formulation for commercial use. With urea present, fast coating rates can be realized at ambient temperature with relatively low hypophosphite levels. The low hypophosphite levels equate to low levels of hydrogen sulfide off-gas.

                  TABLE 3                                                          ______________________________________                                                 Coating        Peel     H.sub.2 S                                              Amount.sup.a   Strength Level                                          Form.   (wt % Sn)      (lb/in)  (ppm)                                          ______________________________________                                         A       NA             4-5       0                                             B       NA             4-5       0                                             C       NA             4-5      1800                                           D       NA             4-5      1900                                           E       NA             NA       600                                            F       NA             NA       300                                            G       21.0           ˜3.2                                                                              1000                                           H       29.4           ˜3.8                                                                              200                                            I       20.1           3.9      150                                            J       13.6           4.0      1200                                           K       19.9           ˜3.8                                                                              200                                            L       22.4           ˜3.85                                                                             100                                            ______________________________________                                          .sup.a Coating amount (weight % Sn) is a measure of tin content as weight      percent tin of a region one micrometer deep from the surface.                  NA = not available, not measured.                                        

                  TABLE 4                                                          ______________________________________                                         Bath A                                                                         Thiourea               60     g                                                Urea                   40     g                                                Tartaric Acid          30     g                                                Glucose                40     g                                                Conc. Sulfuric Acid    20     ml                                               Stannous Sulfate       60     g                                                Triton X-100           20     g                                                Water                  to 1   liter                                            Bath B                                                                         Thiourea               60     g                                                Urea                   0      g                                                Tartaric Acid          30     g                                                Glucose                40     g                                                Conc. Sulfuric Acid    20     ml                                               Stannous Sulfate       60     g                                                Triton X-100           20     g                                                Water                  To 1   liter                                            Bath C                                                                         Water                  600    ml                                               Conc. Sulfuric Acid    200    ml                                               Thiourea               80     g                                                Urea                   40     g                                                Sodium Hypophosphite   40     g                                                Stannous Sulfate       20     g                                                Water                  To 1   liter                                            Bath D                                                                         Water                  640    ml                                               Conc. Sulfuric Acid    200    ml                                               Thiourea               80     g                                                Urea                   0      g                                                Sodium Hypophosphite   40     g                                                Stannous Sulfate       20     g                                                Water                  To 1   liter                                            Bath E                                                                         Water                  600    ml                                               Conc. Sulfuric Acid    200    ml                                               Thiourea               80     g                                                Urea                   20     g                                                Sodium Hypophosphite   16     g                                                Stannous Sulfate       20     g                                                Water                  To 1   liter                                            Bath F                                                                         Water                  600    ml                                               Conc. Sulfuric Acid    200    ml                                               Thiourea               80     g                                                Urea                   40     g                                                Sodium Hypophosphite   5      g                                                Stannous Sulfate       20     g                                                Water                  To 1   liter                                            Bath G                                                                         Water                  400    ml                                               Conc. Sulfuric Acid    200    ml                                               Hypophosphorus                                                                 Acid (50%)             20     ml                                               Thiourea               60     g                                                Urea                   40     g                                                Stannous Sulfate       20     g                                                Water                  To 1   liter                                            Bath H                                                                         Water                  500    ml                                               Conc. Sulfuric Acid    100    ml                                               Hypophosphorus                                                                 Acid (50%)             40     ml                                               Thiourea               60     g                                                Urea                   40     g                                                Stannous Sulfate       20     g                                                Water                  To 1   liter                                            Bath I                                                                         Water                  600    ml                                               Conc. Sulfuric Acid    0      ml                                               Hypophosphorus                                                                 Acid (50%)             80     ml                                               Thiourea               60     g                                                Urea                   40     g                                                Stannous Sulfate       20     g                                                Water                  To 1   liter                                            Bath J                                                                         Water                  400    ml                                               Conc. Sulfuric Acid    200    ml                                               Hypophosphorus                                                                 Acid (50%)             20     ml                                               Thiourea               60                                                      Urea                   0      g                                                Stannous Sulfate       20     g                                                Water                  To 1   liter                                            Bath K                                                                         Water                  500    ml                                               Conc. Sulfuric Acid    100    ml                                               Hypophosphorus                                                                 Acid (50%)             40     ml                                               Thiourea               60     g                                                Urea                   0      g                                                Stannous Sulfate       20     g                                                Water                  To 1   liter                                            Bath L                                                                         Water                  600    ml                                               Conc. Sulfuric Acid    0      ml                                               Hypophosphorus                                                                 Acid (50%)             80     ml                                               Thiourea               60     g                                                Urea                   0      g                                                Stannous Sulfate       20     g                                                Water                  To 1   liter                                            ______________________________________                                    

EXAMPLE 3 Effects of Temperature and Immersion Time Upon the Tin Coating

The effects of temperature and immersion time upon the tin coating were studied for two different immersion tin solutions. Four temperatures (30°, 40°, 50°, and 60° C.) and three immersion times (1.5, 3, and 6 minutes) were used. Compositions of the two immersion tin solutions are given in Table 5 below.

Coupons of copper laminate were coated under the above conditions in the manner described in Example 1. The resulting tin-coated coupons were processed as described in Example 1 and then subjected to EDXA analysis to determine the weight % tin level for each coating. Results are summarized in Table 6 below.

Visually, the coatings appeared to fall in two general classes. The coatings made with bath 1 of Table 5 at all temperatures and with bath 2 of Table 5 at low temperatures (e.g. 30° C.) appeared shiny and uniform. In contrast the coatings with bath 2 of Table 5 at elevated temperatures were noticeably more dull. SEM analysis of the above coatings confirmed that the latter coatings (class 2) had different morphology.

                  TABLE 5                                                          ______________________________________                                         IMMERSION TIN BATHS                                                            ______________________________________                                         Bath 1                                                                         Water                 500    ml                                                Conc. Sulfuric Acid   100    ml                                                Hypophosphorus        40     ml                                                Acid (50%)                                                                     Thiourea              60     g                                                 Urea                  40     g                                                 Stannous Sulfate      20     g                                                 Water                 To 1   liter                                             Bath 2                                                                         Hypophosphorus        80     ml                                                Acid (50%)                                                                     Thiourea              60     g                                                 Stannous Sulfate      20     g                                                 Water                 To 1   liter                                             ______________________________________                                    

                  TABLE 6                                                          ______________________________________                                         Coating Weight Percent Tin Level at Different                                  Temperatures and Immersion Times for Two Different Baths                                                             Instron Peel                                           Temp     Immersion                                                                              Wt %   Strength                                 Sample Bath   (°C.)                                                                            Time (min)                                                                             Sn.sup.a                                                                              (lb/inch)                                ______________________________________                                         1      1      30       1.5     26.8   4.7                                      2      1      30       3.0     42.1   4.6                                      3      1      30       6.0     53.9   5.0                                      4      1      40       1.5     44.2   3.8                                      5      1      40       3.0     54.7   4.7                                      6      1      40       6.0     65.8   5.1                                      7      1      50       1.5     52.7   5.1                                      8      1      50       3.0     64.1   5.3                                      9      1      50       6.0     76.6   5.2                                      10     1      60       1.5     58.4   2.7                                      11     1      60       3.0     68.8   3.5                                      12     1      60       6.0     80.1   2.7                                      13     2      30       1.5     19.0   4.3                                      14     2      30       3.0     21.8   3.5                                      15     2      30       6.0     28.9   3.7                                      16     2      40       1.5     27.1   3.7                                      17     2      40       3.0     39.0   4.2                                      18     2      40       6.0     49.9   4.7                                      19     2      50       1.5     42.4   3.2                                      20     2      50       3.0     51.1   3.6                                      21     2      50       6.0     69.3   3.8                                      22     2      60       1.5     46.5   2.4                                      23     2      60       3.0     59.1   2.3                                      24     2      60       6.0     74.1   2.0                                      ______________________________________                                          .sup.a Wt. % Sn as defined in Table 3                                    

Although the invention has been described by reference to some embodiments, it is not intended that the invention is to be limited thereby but that certain modifications are intended to be included as falling within the scope of the foregoing disclosure and the following claims. 

What is claimed is:
 1. A composition containing components adapted to form an immersion coating composition when said components are admixed together,one of said components comprising (a) a thiourea compound and (b) a urea compound another of said components comprising (c) a metal salt (d) a member selected from the group of hypophosphite salts or a hypophosphorous acid, andsaid metal salt being selected from the group of salts based on the Group IVA metals including tin, Group VIII metals, Group IB metals, Group IIB metals and Group IIIA metals, said metal salt, urea compound and thiourea compound each being present in an amount sufficient to enable said composition to function as an immersion composition.
 2. The composition of claim 1 in which(c) is a tin salt.
 3. The composition of claim 1 in which(c) is stannous sulfate and (e) is sulfuric acid.
 4. The composition of claims 1 or 2 where said metal salt comprises a stannous salt.
 5. The composition of claims 1 or 2 or 3 further comprising a reducing agent.
 6. The compositions of claims 1 or 2 further comprising an acid and said metal salt comprises a stannous salt of a mineral acid.
 7. The composition of claim 1 wherein said thiourea compound and said urea compound comprise a thiourea nucleus and a urea nucleus with the same substituents on each of said nuclei.
 8. The composition of claim 7 where said thiourea compound comprises thiourea and said urea compound comprises urea.
 9. The composition of claims 1 or 2 or 3 further comprising a compound selected from a member of the group consisting of a Group VIII metal salt, a Group IVA metal salt with the exception of tin, a Group IIB metal salt or a Group IB metal salt or mixtures thereof.
 10. The composition of claims 1 or 2 or 3 further comprising a metal salt selected from a member of the group consisting of the salts of iron, cobalt, and nickel or mixtures thereof.
 11. The composition of claims 1 or 2 or 3 further comprising a salt of lead.
 12. The composition of claims 1 or 2 or 3 further comprising a surfactant.
 13. The composition of claims 1 or 2 or 3 further comprising a polyoxyethylene nonyl phenol surfactant.
 14. The composition of claims 1 or 2 or 3 where the components of said composition are present in the following amounts on a molar basis:(a) about 10 to about 125 parts of a thiourea compound; (b) about 10 to about 125 parts of a urea compound; (c) about 1 to about 15 parts of a metal salt.
 15. The composition of claim 14 further comprising 0 to about 40 parts of a chelating agent; about 5 to about 110 parts of a reducing agent and from 0 to about 250 parts of an acid.
 16. The composition of claim 15 further comprising a compound selected from a member of the group consisting of a Group VII metal salt, a Group IVA metal salt with the exception of tin, a Group IIB metal salt or a Group IB metal salt or mixtures thereof in an amount from about 0.2 parts to about 55 parts on a molar basis and said metal salt comprises a tin salt.
 17. An immersion coating formed from the two component composition of claims 1 or 2 or
 3. 18. An immersion coating formed from the two component composition of claims 1 or 2 or 3 further comprising, a chelating agent and a reducing agent.
 19. A process for forming an immersion coating composition which comprisespreforming separate component compositions one of said component compositions comprising (a) a thiourea compound and (b) a urea compound, and another of said component compositions comprising (c) a metal salt; (d) a member selected from the group of hypophosphite salts or hypophosphorous acid,said metal salt being selected from the group of salts based on the Group IVA metals including tin, Group VIII metals, Group IB metals, Group IIB metals and Group IIIA metals, said metal salt, urea compound and thiourea compound each being present in an amount sufficient to enable said composition to function as an immersion composition, then admixing said component compositions together just prior to use as an immersion coating to minimize formation of hydrogen sulfide by the reaction of said components with one another.
 20. A process as in claim 19 in which (c) is a tin salt.
 21. A process as in claim 20 in which (c) is stannous sulfate and which further contains sulfuric acid. 